Abstract:In order to study the surface passivation process of soft magnetic metal powder, gas atomized iron-silicon powder was used as raw material to prepare passivation powder under different passivation conditions, and the passivation powder was pressed into magnetic rings. The surface morphology of passivated powder was observed by scanning electron microscopy (SEM), and the magnetic ring properties were tested. The results show that with the increase of reaction temperature or the decrease of pH value of reaction solution, the density and permeability of the magnetic core decrease, and the insulation resistance and compressive strength increase. Through the comparison of data, the passivation process with high permeability and high insulation resistance is obtained, that is, the mass ratio of Fe-Si powder and aluminum dihydrogen phosphate solution with pH 3.0 is 1∶1, and the reaction is carried out at 50 ℃ for 15 min. The magnetic ring has the best performance, the relative permeability is 36.3, the insulation resistance is 57 mΩ, the density is 7.24 g/cm3, and the compressive strength is 6.0 MPa.
李伟健,李媛媛. 铁硅粉末表面钝化工艺的研究[J]. , 2018, 28(04): 12-16.
LI Wei-jian,LI Yuan-yuan. Study on surface passivation process of iron-silicon powder. , 2018, 28(04): 12-16.
[1] Shokrollahi H , Janghorban K . Soft magnetic composite materials [J]. Journal of Materials Processing Technology , 2007 , 189 : 1 - 12.[2] Laurcnta P , Viaub U , Konna A M , et al . Effect of the magnetic fraction on the complex susceptibility of soft magnetic composite materials [J]. Journal of Magnetismand Magnetic Materials , 1996 , 160 : 63 - 61.[3] Lin Z W , Zhu Z G . Three-dimensional magnetic properties of soft magnetic composite materials . Journal of Magnetic Materials , 2006 , 299 : 29 - 34[4] Bayramli E ,Olgelioglu O , Ertan H B . Powder metal development for electrical motor applications[J]. Journal of Materials Processing Technology , 2005, 161: 83 - 88 [5] Shokrollahi H , Janghorhan K . Fffcct of warm compaction on the magnetic and electrical properties of Fc-based soft magnetic compositcs [J] . Journal of Magnetism and Magnetic Materials , 2007 , 313 : 182 - 186[6] Hcmmati L , Madaah Hosscini H , Kianvash A . The corrclations between processing parameters and magnetic properties of an irorrresin soft magnetic composite [J]. Journal of Magnetism and Magnetic Materials , 2006 , 305 : 117 - 151.[7] 李发长 , 李一 , 贾成厂等. 成型工艺对铁基软磁复合材料电磁性能的影响[J]. 粉末冶金技术 , 2012 ,12 ( 6 ) : 415 - 419[8] Yang B , Wu Z B , et al. High-performance Fe/SiO2 soft magnetic composites for low-loss and high-power applications. Journal of Physics D : Applied Physics , 2010 , 43 (36) :365003 - 1 - 6[9] Jansson Patricia. 交直流用铁粉基软磁材料[J]. 粉末冶金工业, 2001, 11 (11) :11 - 17[10] 田建军, 张德金, 袁勇等. 铁基软磁复合材料成形和热处理工艺研究[J]. 粉末冶金工业, 2011, 21 (4) : 49 - 52[11] 赵莉, 李笃信, 李昆等. 粘结剂对纯铁磁粉芯性能的影响[J]. 粉末冶金工业, 2011, 21 (4) : 42 - 48[12] 田建军, 崔建民, 袁勇等. 磷化工艺制备绝缘软磁粉末及其频率特性研究[J]. 粉末冶金工业, 2010, 20 (5) : 23 - 26[13] 吴深, 孙爱芝, 徐文欢等. 软磁复合材料绝缘处理技术的研究进展[J]. 材料导报, 2013, 27 (5) : 5 – 13[14] 杨明. 新型粘结剂铁基粉末温压成形的研究[D], 2009, 合肥工业大学[17] H Zeng, K. K Chittur, W. R Lace?eld. Analysis of bovine serum albumin adsorption on calcium phosphate and titanium surfaces[J]. Biomaterials 1999, 20(4):84–377.