Effect of hot extrusion on properties of SiC/2024Al composites |
HU Zhi-yong1,YAN Li-peng2,WANG Ai-qin3 |
1. China Airborne Missile Academy, Luoyang 471099, China 2. School of Material and Engineering, He’nan Mechanical and Electrical Engineering College, Xinxiang 453003, China 3. School of Material Science and Engineering, He’nan University of Science and Technology, Luoyang 471099, China |
|
|
Abstract The 35%SiC/2024Al (mass percent) composite was prepared by cold pressing and sintering, and then the specimen was hot-extruded. The microstructure of the material was observed by optical microscope and TEM, the physical and mechanical properties were also tested. The distribution characteristic of SiC particles, change of grains in matrix and the strengthening mechanism of the composite were investigated. The results show that the distribution of SiC particles is more uniform and the segregation decreases after hot-extrusion. The arrangement of SiC particles in the direction of extrusion is more oriental and orderly. The grains of the composite are refined. The densities and tensile strength are increased significantly after hot-extrusion.
|
Received: 30 June 2014
Published: 29 July 2015
|
|
|
|
[1] 兖利鹏, 王爱琴, 谢敬佩,等. SiC含量对SiC/6061Al基复合材料性能的影响[J]. 粉末冶金工业, 2013, 32(137): 30-34.[2] J. A. Hook er, P. J. Doorbar. Metal matrix composites for aeroengines [J]. Materials Science and Technology. 2000, 16: 725-731[3] H. Ismar, F. Schroter, F. Streicher. Effects of Interfacial Debonding on the Transverse Loading Behavior of Continuous Fibre-reinforced Metal Matrix composites[J]. Comp. Lit. Struct, 2001, 79(18): 1713-1733.[4] Contreras A, Angdes-Chdvez C, Flores O, et aL. Structural, morphological and interfacial characterization of A1-Mg/TiC composites. Mater Character, 2007, (58): 685-690.[5] 兖利鹏, 王爱琴, 谢敬佩, 等. 铝基复合材料在汽车领域的应用研究进展[J]. 稀有金属与硬质合金, 2013, 41(2): 44-48.[6] 刘杰, 孙卫和. 碳化硅颗粒增强铝基复合材料的制备工艺进展[J]. 稀有金属与硬质合金, 2008, 36: 59-62[7] 平延磊, 贾成厂, 曲选辉, 等. SiCp/A1复合材料的研究方法现状[J]. 粉末冶金技术. 2005, 23: 296-299[8] 孙有平,严红革,苏斌,等.热挤压喷射沉积Al-SiCp复合材料中SiC粉末特征研究[J].铸造技术, 2012, 33(10): 1145-1148.[9] 李建辉. SiCw/6061复合材料挤压变形对组织性能的影响及机理研究[D].哈尔滨:哈尔滨工业大学博士学位论文, 2006: 46-50[10] 张显峰, 路政, 苏海, 等. 热挤压变形对搅拌铸造SiCp/2024复合材料显微组织与力学性能的影响[J].塑性工程学报,2011, 18(1): 85-90[11] 栾佰峰, 姜龙涛, 孔海宽, 武高辉. 热挤压变形对亚微米Al2O3p/Al复合材料组织性能的影响[ J]. 中国有色金属学报, 2003, 13(2): 373- 374 |
|
|
|