Abstract:The GNPs-Cu/Ti6Al4V composites were prepared by microwave sintering. The effects of copper plated GNPs on the microstructure and mechanical properites of Ti matrix composites were investigated. The results show that a layer of uniformly distributed copper particles is successfully coated on the surface of GNPs. The interfacial reaction between graphene and Ti matrix is serious, and TiC with particle size of 2-5 μm is easily generated. After copper coating, the TiC contents at the interface increase, and the new Ti2Cu phase is also generated. Compared to the GNPs/Ti6Al4V composites, the mechanical properties of the GNPs-Cu/Ti6Al4V are improved. The relative density, micro-hardness and compression strength of GNPs-Cu/Ti6Al4V are up to 95.48%, 468 HV0.1 and 1 406 MPa, respectively. At the same time, the wear mechanism changes from abrasive wear of Ti6Al4V matrix to adhesive wear of GNPs-Cu/Ti6Al4V composites.
收稿日期: 2017-11-03
出版日期: 2018-06-26
通讯作者:
王丽君
E-mail: longino2912@126.com
引用本文:
王丽君. 发动机用石墨烯表面镀Cu增强钛基复合材料的制备及力学性能[J]. , 2018, 28(03): 57-60.
WANG Li-jun. Preparation and mechanical properties of titanium matrix composites reinforced by graphene with Cu-coated for engines. , 2018, 28(03): 57-60.