Abstract：The effect of 0.35 mm cool rolled plate high grade non-oriented electric steel(mass fraction 2.6%~28%) annealing at 800~900 ℃ by box-furnace on structure ,texture and properties was researched. The results showed that with increasing annealing temperature of cool rolled plate, the grain size increased, {111}texture reduced, the best iron loss value was 218 W/Kg at 900 ℃, and the magnetic induction was changed unconspicuous ,decreased from 1685 T at 800 ℃ to1678 T at 900 ℃.