Abstract：Effect of bending direction and thickness on stress relaxation rate of amorphous Fe-based strips was studied. Compared with the free side towarded inside, the stress relaxation rate was higher after annealing under crystallization temperature when the free side towarded out; the stress relaxation rate became higher as the strip thickness decreased.
收稿日期: 2014-11-28
出版日期: 2015-04-21
通讯作者:
付小同
E-mail: 865948936@qq.com
引用本文:
付小同，陈文智，张淑兰，邢彦兴，张艳明. 弯曲方向和带材厚度对铁基非晶合金应力松弛率的影响[J]. , 2015, 22(2): 1-3.
FU Xiao-tong, CHEN Wen-zhi, ZHANG Shu-lan, XING Yan-xing, ZHANG Yan-ming. Effect of bending direction and thickness on stress relaxation rate of amorphous Fe-based strips. , 2015, 22(2): 1-3.