Changes of microstructure and magnetic properties of MM- Fe- B sintered magnets by doping Cu- Al
DU Xiao- hong1, HE Yong- cheng1, ZHANG Xue- feng1,2, LI Yong- feng1, LIU Yan- li1, LIU Fei1
(1. School of Science, Inner Mongolia University of Science & Technology, Baotou 014010, Nei Mongol,China 2. Key Laboratory of Integrated Exploitation of Bayan Obo Multi- Metal Resources, Inner Mongolia University of Science& Technology, Baotou 014010, Nei Mongol,China)
Abstract:The MM- Fe- B magnets prepared by using mixed rare earth metals (MM=La, Ce, Pr, Nd) have low coercivity Hcj. The effects of CuAl and different annealing conditions on MM- Fe- B sintered magnets and the microstructure of MM- Fe- B sintered magnets. It is found that the addition of CuAl enhances the coupling effect of magnet removal and improves the wettability of the MM- rich phase and the main phase. Br=0. 944 T, Hcj=164. 0 kA/m and (BH)max=80. 6 kJ/m3 when CuAl is added to 0. 25%(mass fraction) and the annealing temperature reaches 470 ℃. The coercivity Hcj has the largest change, and the growth rate is 44. 1% compared with the addition of CuAl magnet coercivity Hcj.
杜晓红,何永成,张雪峰 ,李永峰,刘艳丽,刘飞. CuAl掺杂对烧结MM- Fe- B磁体的性能和微观结构的影响[J]. , 2017, 24(6): 18-22.
DU Xiao- hong, HE Yong- cheng, ZHANG Xue- feng,, LI Yong- feng, LIU Yan- li, LIU Fei. Changes of microstructure and magnetic properties of MM- Fe- B sintered magnets by doping Cu- Al. , 2017, 24(6): 18-22.
[1]Sagawa M, Fujimura S, Togawa N, et al.New material for permanent magnets on a base of Nd and Fe[J].J. Appl. Phys, 1984, 55(6):2083-2085
[2]周寿增, 董清飞.超强有磁体—稀土铁系永磁材料(第2版)[M].北京:冶金工业出版社, 2004:282-291
[3]吴树杰, 包小倩, 向丹刚.磁体的组织与磁学性能[J].北京科技大学学报, 2013, 35(6):778-780
[4] Yan M, Ni J J, Ma T Y, et al.Changes of microstructure and magnetic properties of Nd–Fe–B sintered magnets by doping Al–Cu. J. Magn. Magn. Mater, 2011, 323:2549–2553[J].J. Magn. Magn. Mater, 2011, 323:2549-2553[J].J. Magn. Magn. Mater, 2011, 323:2549-2553
[5] Yan M, Ni J J, Ma T Y, et al.Effect of post-sintering annealing on microstructure and coercivity of Al85Cu15-added Nd–Fe–B sintered magnets. J. Magn. Magn. Mater, 2010, 322:3710–3713[J].J. Magn. Magn. Mater, 2010, 322:3710-3713[J].J. Magn. Magn. Mater, 2010, 322:3710-3713
[6] Li Z, Liu W Q, Zha S S, et al.Effects of CE substitution on the microstructures and intrinsic magnetic properties of Nd–Fe–B alloy. J. Magn. Magn. Mater, 2015, 393:551-554.[J].J. Magn. Magn. Mater, 2015, 393:551-554[J].J. Magn. Magn. Mater, 2015, 393:551-554
[7] Zhu M G, Li W, Wang J D, Zheng L Y, et al.Influence of Ce Content on the Rectangularity of Demagnetization Curves and Magnetic Properties of Re-Fe-B Magnets Sintered by Double Main Phase Alloy Method. IEEE Trans. Magn, 2014, 50, (1000104).[J].IEEE Trans. Magn, 2014, 50:-[J].IEEE Trans. Magn, 2014, 50:-
[8]Niu E, Chen Z A, Chen G A, et al.Achievement of high eoecrivity in sintered R-Fe-B magnets based on misch-metal by dual alloy method[J].J. Appl. Phys, 2014, 115(113912):1-4
[9] Yan M, Jin J Y, Zhang Y J, et al.Chemically Inhomogeneous RE-Fe-B Permanent Magnets with High Figure of Merit: Solution to Global Rare Earth Criticality. Scientific Reports, 2016, 6, 32200.[J].Scientific Reports, 2016, 6(32200):-
[10] Yu X Q, Yue M and Liu W Q, et al.Structure and intrinsic magnetic properties of MM2Fe14B(MM=La, Ce, Pr, Nd) alloys.J. Rare Earths, 2016, 34(6), 614-617.[J].J. Rare Earths, 2016, 34(6):614-617